Chemical vapor deposition (CVD) is a chemical process used to produce high-purity, high-performance solid materials. The process is often used in the semiconductor industry to produce thin films. In a typical CVD process, the wafer (substrate) is exposed to one or more volatile precursors, which react and/or decompose on the substrate surface to produce the desired deposit. Frequently, volatileby-products are also produced, which are removed by gas flow through the reaction chamber.

Microfabrication processes widely use CVD to deposit materials in various forms, including: monocrystallinepolycrystallineamorphous, and epitaxial. These materials include: siliconcarbon fiber,carbon nanofibersfilamentscarbon nanotubesSiO2silicon-germaniumtungstensilicon carbidesilicon nitridesilicon oxynitridetitanium nitride, and various high-k dielectrics. The CVD process is also used to produce synthetic diamonds.


Picture
Picture
Types of chemical vapor deposition

A number of forms of CVD are in wide use and are frequently referenced in the literature. These processes differ in the means by which chemical reactions are initiated (e.g., activation process) and process conditions.

  • Classified by operating pressure
    • Atmospheric pressure CVD (APCVD) - CVD processes at atmospheric pressure.
    • Low-pressure CVD (LPCVD) - CVD processes at subatmospheric pressures.[1] Reduced pressures tend to reduce unwanted gas-phase reactions and improve film uniformity across the wafer. Most modern CVD processes are either LPCVD or UHVCVD.
    • Ultrahigh vacuum CVD (UHVCVD) - CVD processes at a very low pressure, typically below 10−6 Pa (~10−8 torr). Note that in other fields, a lower division between high and ultra-high vacuum is common, often 10−7 Pa.
  • Classified by physical characteristics of vapor
    • Aerosol assisted CVD (AACVD) - A CVD process in which the precursors are transported to the substrate by means of a liquid/gas aerosol, which can be generated ultrasonically. This technique is suitable for use with non-volatile precursors.
    • Direct liquid injection CVD (DLICVD) - A CVD process in which the precursors are in liquid form (liquid or solid dissolved in a convenient solvent). Liquid solutions are injected in a vaporization chamber towards injectors (typically car injectors). Then the precursor vapors are transported to the substrate as in classical CVD process. This technique is suitable for use on liquid or solid precursors. High growth rates can be reached using this technique.
  • Plasma methods (see also Plasma processing)
    • Microwave plasma-assisted CVD (MPCVD)
    • Plasma-Enhanced CVD (PECVD) - CVD processes that utilize plasma to enhance chemical reaction rates of the precursors.[2] PECVD processing allows deposition at lower temperatures, which is often critical in the manufacture of semiconductors.
    • Remote plasma-enhanced CVD (RPECVD) - Similar to PECVD except that the wafer substrate is not directly in the plasma discharge region. Removing the wafer from the plasma region allows processing temperatures down to room temperature.
  • Atomic layer CVD (ALCVD) – Deposits successive layers of different substances to produce layered, crystalline films. See Atomic layer epitaxy.
  • Combustion Chemical Vapor Deposition (CCVD) - nGimat's proprietary Combustion Chemical Vapor Deposition process is an open-atmosphere, flame-based technique for depositing high-quality thin films and nanomaterials.
  • Hot wire CVD (HWCVD) - also known as catalytic CVD (Cat-CVD) or hot filament CVD (HFCVD). Uses a hot filament to chemically decompose the source gases.[3]
  • Metalorganic chemical vapor deposition (MOCVD) - CVD processes based on metalorganic precursors.
  • Hybrid Physical-Chemical Vapor Deposition (HPCVD) - Vapor deposition processes that involve both chemical decomposition of precursor gas and vaporization of a solid source.
  • Rapid thermal CVD (RTCVD) - CVD processes that use heating lamps or other methods to rapidly heat the wafer substrate. Heating only the substrate rather than the gas or chamber walls helps reduce unwanted gas phase reactions that can lead to particle formation.
  • Vapor phase epitaxy (VPE)

Substances commonly deposited for ICs

This section discusses the CVD processes often used for integrated circuits (ICs). Particular materials are deposited best under particular conditions.

PolysiliconPolycrystalline silicon is deposited from silane (SiH4), using the following reaction:

SiH4 → Si + 2 H2This reaction is usually performed in LPCVD systems, with either pure silane feedstock, or a solution of silane with 70-80% nitrogen. Temperatures between 600 and 650 °C and pressures between 25 and 150 Pa yield a growth rate between 10 and 20 nm per minute. An alternative process uses a hydrogen-based solution. The hydrogen reduces the growth rate, but the temperature is raised to 850 or even 1050 °C to compensate.

Polysilicon may be grown directly with doping, if gases such as phosphinearsine or diborane are added to the CVD chamber. Diborane increases the growth rate, but arsine and phosphine decrease it.


Silicon dioxideSilicon dioxide (usually called simply "oxide" in the semiconductor industry) may be deposited by several different processes. Common source gases include silane and oxygendichlorosilane (SiCl2H2) and nitrous oxide (N2O), ortetraethylorthosilicate (TEOS; Si(OC2H5)4). The reactions are as follows:

SiH4 + O2 → SiO2 + 2 H2SiCl2H2 + 2 N2O → SiO2 + 2 N2 + 2 HClSi(OC2H5)4 → SiO2 + byproductsThe choice of source gas depends on the thermal stability of the substrate; for instance, aluminium is sensitive to high temperature. Silane deposits between 300 and 500 °C, dichlorosilane at around 900 °C, and TEOS between 650 and 750 °C, resulting in a layer of low- temperature oxide (LTO). However, silane produces a lower-quality oxide than the other methods (lower dielectric strength, for instance), and it deposits nonconformally. Any of these reactions may be used in LPCVD, but the silane reaction is also done in APCVD. CVD oxide invariably has lower quality than thermal oxide, but thermal oxidation can only be used in the earliest stages of IC manufacturing.

Oxide may also be grown with impurities (alloying or "doping"). This may have two purposes. During further process steps that occur at high temperature, the impurities may diffuse from the oxide into adjacent layers (most notably silicon) and dope them. Oxides containing 5–15% impurities by mass are often used for this purpose. In addition, silicon dioxide alloyed with phosphorus pentoxide ("P-glass") can be used to smooth out uneven surfaces. P-glass softens and reflows at temperatures above 1000 °C. This process requires a phosphorus concentration of at least 6%, but concentrations above 8% can corrode aluminium. Phosphorus is deposited from phosphine gas and oxygen:

4 PH3 + 5 O2 → 2 P2O5 + 6 H2Glasses containing both boron and phosphorus (borophosphosilicate glass, BPSG) undergo viscous flow at lower temperatures; around 850 °C is achievable with glasses containing around 5 weight % of both constituents, but stability in air can be difficult to achieve. Phosphorus oxide in high concentrations interacts with ambient moisture to produce phosphoric acid. Crystals of BPO4 can also precipitate from the flowing glass on cooling; these crystals are not readily etched in the standard reactive plasmas used to pattern oxides, and will result in circuit defects in integrated circuit manufacturing.

Besides these intentional impurities, CVD oxide may contain byproducts of the deposition process. TEOS produces a relatively pure oxide, whereas silane introduces hydrogen impurities, and dichlorosilane introduces chlorine.

Lower temperature deposition of silicon dioxide and doped glasses from TEOS using ozone rather than oxygen has also been explored (350 to 500 °C). Ozone glasses have excellent conformality but tend to be hygroscopic – that is, they absorb water from the air due to the incorporation of silanol (Si-OH) in the glass. Infrared spectroscopy and mechanical strain as a function of temperature are valuable diagnostic tools for diagnosing such problems.

5/18/2011 11:23:17 am

Very like watching your blog, content is very fascinating, I'm looking forward to more of your work, I have paid attention to you.

Reply
6/6/2011 08:05:21 pm

Viewing that we've been exploring for the when for just a helpful view in relation to this particular concept . Exploring in Aol I at last uncovered out this web page. Seeing this I'm happy to say that I've got an exquisite uncanny feeling I identified the really details I required. Most surely i'll make sure to bear in mind this web page and check out it out regularly.

Reply
9/26/2012 08:27:38 pm

will be restored soon

Reply



Leave a Reply.